ASTM A270 sanitary tubing,A270 Sanitary Pipe

2018-06-26

Kaysen stainless steel sanitary pipe is manufactured in accordance with ASTM A270 sanitary standards. Our stainless steel sanitary pipe is made from cold rolled stainless steel strip whose chemical elements are specially controlled to enhance weldability. The weld bead is cold-worked to a full finished condition, resulting in a virtually undetectable longitudinal weld. Bright annealing to 1,900°F minimum follows in a controlled atmosphere to preserve maximum structural integrity. The tubes are then mechanically polished to a 180 grit (20 μ-in. Ra maximum) interior and 150 grit (32 μ-in. Ra maximum) exterior finish via kaysen's state-of-the-art process. Stainless Steel Sanitary Pipes are then line-stenciled with OD, wall, ASTM specifications, grade, and heat number. Price and weight is per foot.

About ASTM A270 sanitary tubing

ASTM A 262: Methods of detecting intergranular corrosion for the magnetization coefficient.
ASTM A 480/A 480 M is the general specifications for flat stainless steel, heat-resistant stainless steel plate, sheet and steel bars.
ASTM A 923 Test methods for detecting detrimental intermetallic phase in duplex austenitic/ferritic stainless steels
ASTM A 967 is the specification of passivation treatment for stainless parts .
ASTM A 1016/1016 M is the general specification for ferritic alloy steel, austenitic alloy steel and stainless steel.
E 527 is the test methods for numbering metal and alloy
ASTM B 46.1 surface structure (surface roughness, waviness and layers).

ASME boiler and pressure vessel`s numbers and other standards.

ASTM A270 Sanitary stainless steel tubing specification
ASTM A270 sanitary (hygienic) stainless steel tubing is the standard specification for the welded seamless, and heavily cold worked welded austenitic and ferritic stainless steel sanitary tubing. It includes the stainless steel tube types in seamless and welded ERW, EFW. ASTM A270 sanitary tubing intended applied in the diary and food industry, bio processing equipment, and having special surface finish.

SURFACE REQUIREMENTS
Surface of rolled products: No need extra polishing or smooth treatment.
Mechanical polished surface: Purchasers according the same numbering abrasive (grinding stuff) to polish the products get the required products` surface.
Electrolytic polishing of the surface: Before this processing, manufacturer could use other ways to polish products.
The maximum average of roughness: Customers could specify the maximum roughness of internal surface, external surface and both surface.
Normally surface treatment: Internal, External, SF4, SF3, etc.

View here for about information about ASTM A270 Standard Specification.

ASTM A270 stainless steel tube size range
ASTM A270 sanitary stainless pipe usually refers to the small pipe diameters, normally from 1/2" to 2 1/2", thickness from 0.049 in (1.24mm) to 0.15 in (3.81mm).
The maximum outer diameter of ASTM A270 tubing is 12 inches (304.8 mm).
ASTM A270 tubing using inch-pound as the standard unit of measure.
Wall thickness tolerance shall not vary more than 12.5%.

Stainless tube manufacturing processes
ASTM A270 sanitary stainless steel pipe shall be noted below points during manufacturing processes:
1) Seamless steel pipe should not contains any kind of welding processing.
2) Welded steel pipe applied in automatic welding processing, but should not use metal materials as filler.
3) Heavily cold worked (HCW) tubes shall be manufactured by cold working of not less than 35% reduction of thickness of both wall and weld to a welded pipe prior to the final anneal. Filler materials shall be noted added during welding process. The weld shall be 100% radio graphically inspected in accordance with ASME boiler and pressure vessel standards specification.
4) Sanitary pipe could be furnished with hot finished or cold finished at Manufacture`s option.

Hot-treatment methods for ASTM A270 stainless tube
All materials should supply after hot-treatment. Except the for duplex stainless steel materials S31803, S32003, S320205, S32750, N08926 and N08367, in these cases it shall consist of heating the material to a minimum temperature of 1900 ℉ (1040 ℃) and quenching in water or rapid cooling by other means.

CHEMICAL COMPOSITION
A little part of flat or steel pipe shall be taken for chemical analysis. The composition should meet the ASTM A270 standard table 1.

MECHANICAL TESTS
Mechanical tests includes negative flattening test, hydrostatic or nondestructive electric test. Mechanical strength shall be complied with ASTM A270 standard specification table S2.1.

MARKS
At last, the mark should furnished in accordance with A 1016/A1016M, and specified in the order. Includes the sanitary stainless steel pipe manufactured in Seamless (SML), Welded (WLD) or heavily cold worked (HCW).

PACKAGE
Before delivery, all steel pipes should bundled well, and covered by paper, cloths. Or packed in box by manufacturer.

ADDITIONAL REQUIREMENTS
In case specified in the order, intergranular corrosion tests shall be performed by manufacturer on specimens representative of the as-shipped condition. Sanitary stainless steel pipe and tube shall be capable of passing corrosion tests in the as-shipped condition. For austenite alloy steel should meets the Practice E of the standard A262 , and for duplex alloy steels (S31803, S32205 and A32750) should meets experiment C of Test Methods A 923.